Product Code:SAE AMSB20148
Title:Brazing Sheet, Aluminum Alloy
Issuing Committee:Ams D Nonferrous Alloys Committee
Scope:This specification covers aluminum alloy brazing sheet for use in brazed aluminum joints.
Title:Brazing Sheet, Aluminum Alloy
Issuing Committee:Ams D Nonferrous Alloys Committee
Scope:This specification covers aluminum alloy brazing sheet for use in brazed aluminum joints.
下载地址: 点击此处下载
上一篇: SAE AMS6476 Steel, Bars, Forgings, and Tubing, 0.50Cr - 0.12Mo (0.89 - 1.01C)
下一篇: SAE AS5725 Interface Standard, Miniature Mission Store Interface
下一篇: SAE AS5725 Interface Standard, Miniature Mission Store Interface
基本信息
| 标准名称： | 永磁旋转搅拌高压釜 控制器 |
| 英文名称： | High pressure autoclave with permanent rotary stirrer controller |
| 中标分类： | 仪器、仪表 >> 实验室仪器与真空仪器 >> 实验室基础设备 |
| ICS分类： | 化工技术 >> 分析化学 >> 化学实验室、实 |
| 替代情况： | ZB N61007-1988 |
| 发布部门： | 国家机械工业局 |
| 发布日期： | 1999-08-06 |
| 实施日期： | 2000-01-01 |
| 首发日期： | 1900-01-01 |
| 作废日期： | 1900-01-01 |
| 提出单位： | 长沙科学仪器研究所 |
| 归口单位： | 长沙科学仪器研究所 |
| 起草单位： | 长沙科学仪器研究所 |
| 出版社： | 机械工业出版社 |
| 出版日期： | 2000-01-01 |
| 页数： | 7页 |
| 批文号： | 国机管[1999]422 |
适用范围
本标准规定了永磁旋转搅拌高压釜控制器(以下简称控制器)的技术要求、试验方法、检验规则、标志、包装和贮存。
本标准适用于最大容积不大于101,最大设计压力不大于31MPa的奥氏体不锈钢制高压釜控制器。
本标准与JB/T9509.1一1999《永滋旋转搅拌高压釜釜体》配套使用。
前言
没有内容
目录
没有内容
引用标准
没有内容
所属分类： 仪器 仪表 实验室仪器与真空仪器 实验室基础设备 化工技术 分析化学 化学实验室 实
【英文标准名称】:StandardPracticeforSpecifyinganEquivalent3-SecondDurationDesignLoadingforBlastResistantGlazingFabricatedwithLaminatedGlass【原文标准名称】:用夹层玻璃制造的防爆玻璃窗的等效3秒持续时间设计负荷规定的标准实施规范
【标准号】:ASTMF2248-2009
【标准状态】:现行
【国别】:美国
【发布日期】:2009
【实施或试行日期】:
【发布单位】:美国材料与试验协会(US-ASTM)
【起草单位】:F12.10
【标准类型】:(Practice)
【标准水平】:()
【中文主题词】:
【英文主题词】:airblastpressure;blastresistantglazing;explosion;insulatingglass;laminatedglass;specifieddesignload;Annealedglass;Blast-resistantmaterials/applications;Chemically-strengthenedflatglass;Explosions/explosives;Fully-tempered(FT)flatg
【摘要】:Thispracticeprovidesadesignloadsuitableforsizingblastresistantglazingcomprisedoflaminatedglassorinsulatingglassfabricatedwithlaminatedglass.Blastresistantglazingcomprisedoflaminatedglassorinsulatingglassfabricatedwithlaminatedglassshallbesizedtoresistthe3-seconddurationequivalentdesignloadingfromthisstandardpracticeusingtheproceduresdescribedinPracticeE1300.Blastresistantglazingcomprisedoflaminatedglassorinsulatingglassfabricatedwithlaminatedglasssizedusingthe3-seconddesignloadingdeterminedfromthispracticewillfracturesafelyintheeventofablast,thusreducingthepotentialforpersonalinjury,structuralandnon-structuralbuildingdamage,andcleanupcostsshouldanexplosionoccur.Intheeventablastloadingneveroccurstoblastresistantglazingcomprisedoflaminatedglassorinsulatingglassfabricatedwithlaminatedglasssizedusingthe3-seconddurationloadingdeterminedherein,theblastresistantglazingwillhaveaprobabilityofbreakagelessthanorequalto8litesper1000atthefirstoccurrenceofaloadingequaltothe3-seconddurationdesignloadingdeterminedherein.Blastresistantglazingdesignedtoresistthe3-secondequivalentloadasdeterminedherein,properlysupported,willperformtominimalhazardasdefinedinTestMethodF1642.1.1Thispracticesetsforthamethodtospecifyanequivalent3-seconddesignloadingsuitabletousewithPracticeE1300toselectthethicknessandtypeofblastresistantglazingfabricatedwithlaminatedglasstoglazeafenestration.Glasspliesusedtoconstructlaminatedglassarerecommendedtobeeitherannealedorheatstrengthenedglass.1.2Thispracticeappliestoblastresistantglazingfabricatedusinglaminatedglassonly,includingsinglelaminatedglassandinsulatingglassfabricatedwithlaminatedglass.Asaminimum,insulatingglassshalluselaminatedglassfortheinboard(protectedside)lite.1.3Thispracticeassumesthatblastresistantglazingshallbeadheredtoitssupportingframeusingstructuralsiliconesealantoradhesiveglazingtape.Thewidthofthestructuralsiliconesealantbeadshallbeatleastequaltothelargerof10-mm(3/8-in.)orthethicknessdesignationoftheglasstowhichitadheresbutnotlargerthantwotimesthethicknessdesignationoftheglasstowhichitadheres.Theminimumthicknessofthestructuralsiliconebeadshallbe5-mm(3/16-in.).Thewidthofglazingtapeshallbeatleastequaltotwotimesbutnotmorethanfourtimesthethicknessdesignationoftheglasstowhichitadheres.ThewidthofsiliconeorglazingtapeisreferredtoasbiteandisshownanddiscussedinGuideC1564.1.4Thispracticeassumesthatthestructuralsiliconebeadorglazingtapeisappliedtobothsidesofsinglelitelaminatedglassbutneedonlybeappliedtotheinboardside(protectedside)ofinsulatingglass.1.5ThispracticeassumestheframingmembersshallrestrictdeflectionsofedgesofblastresistantglazingtheysupporttoL/60under2.0x00D7;theloadresistanceoftheblastresistantglazingforinwardloading,whereLdenotesthelengthofthesupportededge.1.6Thispracticeassumestheframingsystemsupportingtheblastresistantglazingsha......
【中国标准分类号】:Q34
【国际标准分类号】:81_040_30
【页数】:4P.;A4
【正文语种】:英语